Zinc Aluminum Magnesium Steel Sheet Coil: The Ultimate Solution for High-Performance Applications

Product Name:  Zinc Aluminum Magnesium SteeL Sheet Coil for Solar Bracket
The Zinc Aluminum-Magnesium coated steel is a new product in the global steel trading industry. It is a result of various extensive steel manufacturing researches done to enable steelmakers to produce coated steel that is better than galvanized steel. 

Product Advantages

Zinc Aluminum Magnesium Coated Steel is an incredible brand product that lasts a lot longer even in the harshest environment settings, has built-in rust prevention on the cut edges and excellent press formability, and reduces the manufacturing cost by requiring less maintenance.

1.Highly resistant to steel corrosion
The non-oxidizing chemical properties of magnesium added to the traditional hot-dip zinc coating steel sheet make it up to 20 times more resistant to corrosion. Also, up to eight times more resistant compared to hot-dip zinc steel sheets coated with 5% aluminum alloy. 
2.Excellent Press Formability
The steel sheets of Zinc Aluminum Magnesium are built with a firmer and smoother coating surface compared to those made from hot-dip zinc coating. This is the reason why Zinc Aluminum Magnesium coated steel sheets do not crack during forming conditions. After the shaping process, the flange area is also reduced.
3.Reduces manufacturing costs significantly
Zinc Aluminum Magnesium coated steel helps save manufacturing costs notably in a variety of ways. Again, because of its enhanced corrosion resistance, it allows life cycle cost reduction. It also allows for upfront cost savings through process omission.
4.Other properties
Product Longevity Zinc Aluminum Magnesium coated steel sheets are more sustainable than other steel products.Light coating weight  Plate thickness is only at 3.2 millimeters, but firmer Environment-friendly All product treatments adhere to environmental requirements, including RoHS directives to avoid the dangers of electrical waste disposal, and ELV systems to ensure that the system is controlled at a low voltage.

Saves coating and transportation costs  Zinc Aluminum Magnesium contributes to cost reduction and shortens delivery time by eliminating the post-hot-dip galvanizing process.Zinc Aluminum Magnesium coated steels may be produced in a wide range of forms for different types of construction projects. It may be formed into a corrugated sheet, punching metal, non-slip metal, lightweight structural steel, pre-notched shaped steel, square pipes, and round pipes. 
Zinc Aluminum Magnesium can be used for road construction such as building railings and other civil engineering projects. It may also be utilized for farming projects such as establishing a greenhouse, compost house, or fish preserve. Lastly, Zinc Aluminum Magnesium® coated steels are also utilized in railroad and housing structures, the building of electric power equipment and automobile parts, and other applications.
 

Comparison With GI Coil

Galvanizing is a production method in which steel or iron is applied with a zinc coating to provide protection against corrosion or rusting. This technique, most especially the hot-dip galvanizing method, is widely used in manufacturing steel products.

Zinc Aluminum Magnesium coated steel sheets outperform galvanized and hot-dip zinc with 5% Al coated steel sheets in terms of red rust resistance. To prove this, Zinc Aluminum Magnesium products underwent outdoor exposure tests with galvanized and hot-dip zinc 5% Al steels in a rural environment and a coastal environment .

The exposure test lasted for a span of 8 months. In the rural setting, results revealed that the corrosion loss of Zinc Aluminum Magnesium coated steel is only at approximately 16-24 gsm, while zinc with 5% Al coated steel is at 38-51 gsm, and the galvanized steel is at 76-89 gsm.
In the coastal environment, the corrosion loss result of Zinc Aluminum Magnesium coated steels is 33-43 gsm, zinc with 5% Al coated steel is at 66-82 gsm, and the galvanized steel is at a high rate of ~105-115 gsm.
In conclusion, Zinc Aluminum Magnesium coated steels are up to four times more corrosion-resistant than galvanized and hot-dip zinc 5% Al coated steels.